LCP(液晶聚合物#)/G-930/美国苏威

Solvay Specialty Polymers Xydar® G-930 Liquid Crystal Polymer (LCP), 30% Glass Fiber

Material Notes:  Xydar® G-930 Liquid Crystal Polymer (LCP) is a glass reinforced injection molding grade developed specifically for electrical/electronic applications utilizing surface mount technology.
The moldability of this resin is exceptional. Xydar® G-930 can fill very thin walls over long flow lengths with little or no flash, even at mold temperatures below 200°F (93°C). In addition, it has low warpage in molded products and exceptional weld line strength.

Features:: Flame Retardant; Good Chemical Resistance; Good Moldability; Good Weather Resistance; High Stiffness; High Strength; Low Warpage; Radiation (Gamma) Resistant

Uses: Automotive Applications; Automotive Electronics; Bobbins; Electrical Parts; Electrical/Electronic Applications; Industrial Applications; Industrial Parts

Automotive Specifications ASTM D5138 LCP0110 G30 B00000; DELPHI M-5282 M5282 Color: BK Black

Information provided by Solvay Specialty Polymers.
 

 

重要参数:

Physical Properties Metric English Comments
Density  1.60 g/cc 0.0578 lb/in³ ASTM D792
Filler Content  0.3 0.3 Glass Fiber
Water Absorption  <= 0.100 % <= 0.100 % ISO 62
  @Time 86400 sec @Time 24.0 hour  
       
Mechanical Properties Metric English Comments
Tensile Strength  135 MPa 19600 psi ASTM D638
Elongation at Break  0.016 0.016 ASTM D638
Tensile Modulus  15.9 GPa 2310 ksi ASTM D638
Flexural Strength  172 MPa 24900 psi ASTM D790
Flexural Modulus  13.4 GPa 1940 ksi ASTM D790
Izod Impact, Notched  0.960 J/cm 1.80 ft-lb/in ASTM D256
Izod Impact, Unnotched  4.30 J/cm 8.06 ft-lb/in ASTM D256
       
Electrical Properties Metric English Comments
Volume Resistivity  1.00e+16 ohm-cm 1.00e+16 ohm-cm ASTM D257
Dielectric Constant   3.9 3.9 ASTM D150
  @Frequency 1.00e+6 Hz @Frequency 1.00e+6 Hz  
  4.2 4.2 ASTM D150
  @Frequency 60.0 Hz @Frequency 60.0 Hz  
Dielectric Strength  39.0 kV/mm 991 kV/in ASTM D149
  @Thickness 1.57 mm @Thickness 0.0618 in  
Arc Resistance  >= 300 sec >= 300 sec ASTM D495
Comparative Tracking Index  185 V 185 V ASTM D3638
       
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  3.60 - 7.20 µm/m-°C 2.00 - 4.00 µin/in-°F  
CTE, linear, Transverse to Flow  40.0 - 79.0 µm/m-°C 22.2 - 43.9 µin/in-°F ASTM D696
Deflection Temperature at 1.8 MPa (264 psi)  271 °C 520 °F Unannealed; ASTM D648
UL RTI, Electrical  220 °C 428 °F  
  @Thickness 0.750 mm @Thickness 0.0295 in  
UL RTI, Mechanical with Impact  200 °C 392 °F  
  @Thickness 0.750 mm @Thickness 0.0295 in  
UL RTI, Mechanical without Impact  220 °C 428 °F  
  @Thickness 0.750 mm @Thickness 0.0295 in  
Flammability, UL94  V-0 V-0  
  @Thickness 0.400 mm @Thickness 0.0157 in  
       
Processing Properties Metric English Comments
Melt Temperature  321 - 360 °C 610 - 680 °F  
Mold Temperature  65.6 - 93.3 °C 150 - 200 °F  
Drying Temperature  149 °C 300 °F  
  @Time 21600 - 28800 sec @Time 6.00 - 8.00 hour  
       
Descriptive Properties      
Availability Asia Pacific    
  Europe    
  North America    
Clamp Tonnage 2.8 to 5.5 kN/cm²    
Color Black; Natural    
Form Pellets    
Processing Technique Injection Molding    
RoHS Compliance RoHS Compliant    
Screw Compression Ratio 2.5:1.0 to 3.0:1.0    
Screw L/D Ratio 20.0:1.0 to 24.0:1.0    

生产厂商:美国苏威先进聚合物公司 [查看报价]

 

产品特性:高温电气 / 电子装配:能承受 SMT 装配工序操作,包括无铅回流焊接。 卓越的暖老化性能,在高温下保持固有特性。 卓越的流动性 - 薄壁,复杂的形状。 尺寸稳定性极佳,模塑收缩率低,热膨胀系数极小,可与金属相媲美。 在成型时,分子链朝着流动的方向排列,产生一种好似其分子自身将其增强的自增强效果可获得极高的强度和弹性模量。 优异的耐化学腐蚀性。 模塑速度:周期循环极快。 卓越的抗蠕变性。 阻燃性。 在宽广的温度范围内具有卓越的介电性